Alkaline anion exchange membrane 60 μmAEM

  LiMo Technology is committed to solve the problem of bottle-neck in the field of new energy membrane materials, and has realized the production of anion exchange membrane (AEM) with high alkaline stability.

Compared with state-of-the-art AEMs, LIMO-AEM has better comprehensive performance, including high alkaline stability, high ionic conductivity, low resistance, high mechanical strength, and high dimensional stability. It is suitable for working at high temperature and in high alkaline concentrated solution. AEM is widely used in fuel cells, hydrogen production by water electrolysis, CO₂ reduction, redox flow batteries, lithium ion extraction, waste acid recovery, seawater desalination by osmotic power generation and other fields.

Technical parameters

Dry thickness (um) 15-80

The tensile strength (MPa) >30

Young's modulus (MPa)>1000

Elongation at break is 6-30%

Water uptake (25-80 ℃) 10-25%

Swelling rate (25-80 ℃) 5-15%

Ion exchange capacity (meq/g) 2-2.5

Ionic conductivity (mS/cm,OH^-) 120-160 (80℃)

The surface resistance (Ω^.cm², OH^-) 0.1-0.15

Alkaline stability (h,5M KOH, 80 ℃) >2000

The size of the membrane can be customized according to requirements.

Membrane treatment

For the required anion, the membrane is immersed in the desired anionic solution, such as sodium chloride, sodium hydroxide, sodium bicarbonate, etc., for more than 1 hour, and then rinsed with deionized water.